910 Alloy

910 Alloy
Users' rating
0

No votes yet

Manufacturer Taulman 3D
Technology FFF / FDM
Generic material Polymer
Materials PA
Suitable for Home, Office, Lab, Training, Prosumers
Purpose Home
Price USD $80.00 USD
Density
UTS Max 55.90MPa
UTS Min 55.90MPa
Tensile Modulus Max 503.00MPa
Tensile Modulus Min 503.00MPa
Elongation at break Max 31.00%
Elongation at break Min
Flexural Modulus Max
Flexural Modulus Min
Flexural Strength Max
Flexural Strength Min
Glass Transition Temp Max 82.00ºC
Glass Transition Temp Min 82.00ºC
Hardness Max
Hardness Min
Hardness Shore Scale
HDT Max
HDT Min
Flammability
USP Class VI Certified
Link

Description

Alloy 910 is a measurable advancement in 3D Printing materials technology from taulman3D.  taulman Alloy 910 is the combined effort of chemical companies, extrusion manufactures and taulman3D to specifically develop a single material to meet as many high performance 3D Printing needs as possible.  With a combined tensile strength higher than the strongest co-polyesters, the durability of Nylons, a shrinkage factor that rivals our t-glase, a vast range of chemical resistance and a 95C working range, you now have one solution easily printable at 245C.

Specifications:

Tensile Strength = 8,100PSI

Modulus PSI = 72,932

Max Elongation at break = 31%

Print Temperature = 245C - 250C

Nozzle size = Any - There are no particulates or additives in Alloy 910

Tg = 82C

Print Bed =

            Cold = BuildTak with coat of PVA

            Hot = Glass heated to 45C with coat of PVA

(PVA is 50% water  and 50% "Elmers Glue All")

Shrinkage = 0.0033   in/in

Transmission = 75%

Color = Clear w/Subtle Amber - May be dyed with acid based dyes.

Availability = 1.75mm and 2.85mm Material is on-hand and shipping worldwide now.